High-temperature resistance corrosion protection for light metals
Product Description
The coating material produces a mechanically resistant coating with a high asset liability on light metals. The surface system generates matte coating with good abrasion resistance, and good resistance to high temperatures (up to 450C) and corrosive media, such as acidic and alkaline condensates.
Drying process and hardening: Processing with at least + 5°C
Application: Spray, paint, dip
Gross density: at the moment not available
Main areas of application
Material Basis:
- Inorganic-Organic 2-K Hybrid System, Solvent-Based
Color:
- Hardened beige-matt
PH-Values:
- < 7, light acid
Package Sizes:
- 5-L-PE Canister 5 kg.
- Further package/container sizes available upon request
Storage
Minimum of 6 months at a temperature from 5 degrees Celsius to 20 degrees Celsius when stored in tightly sealed original container. Protect against frost and higher temperatures. In the event of storage beyond expiration date, test the material prior to use. Tightly air seal opened containers to preserve product life. Ensure sufficient ventilation in product storage areas.
Preparation
Add the individual components after stirring or mixing in a mixing ratio of A : B = 30 : 1. For further details, see separate instructions for use.
Application: As a general rule, spray on or dip coat. For further details see separate instructions for use.
Application Temperatures:
Air and object surface temperature from 5 degrees Celsius to 35 degrees Celsius. Variations from these external conditions could influence the hardening time. Dry within a maximum of 24 hours. Coated surface is chemically resistant after approximately 1 week.
Use and Application:
- The use and application is dependent upon harshness of surface and application procedures.
Protective Measures
During application and use, carefully follow the instructions, safety advice and the pertinent safety and accident instructions of appropriate occupational and trade associations. For further detailed instructions, see safety data sheets.
Cleaning of Tools:
- Clean tools thoroughly with thinner and towel.
Improvement and Second Coatings:
- Mechanically through abrasive finishing (ie., sandpaper) or through emplacement in a bath of lime potash and 2-Propanol.
Disposal:
- Dispose of material residues according to local and/or state regulation for paints and lacquers.
Technical Data
Salt Spray (DINN EN ISO 9227 NSS): 1000h
CASS (DIN EN ISO CASS): 240h
Filoform Corrosion (DIN EN 3665): o.k. no infiltration
Weathering (DIN EN 4892-3: 500h)
4h UV-B 60 Degrees: 4h
Water condensation 50 Degrees C.
Climate Change DBL 7906: 15 min 5 Cycles
23 Degrees C, 4h 80 Degrees C;
30 min 40 Degrees C 98% humidity.
Acid/Base Resistance: pH 1 to pH 11
Pencil Hardness: HB
Tabertest (CS10 F Roll; 8 mg)
1000 rotations per minute
Temperature Resistance: Continuous up to 450 degrees C.