NewPro Nano-Lacquer for Mega-Protection

Roomtemperature curing non-stick system for process optimization

Product Description

With the help of the nano-technology modified ambient temperature-Hardening PU-lacquer with non-adhesive characteristics. Newpro Nanolacquer is an Easy-to-Clean coating. Suitable surfaces are: metal, chrome/nickel-steel, copper, aluminum, resin, GFK, wood/stone and mineral surfaces.

Main areas of application

Protection of metal surfaces for industrial plant components. Coated aluminum and stainless steel surfaces are easier to clean free of printing ink and lacquer stains. Further applications include removal from production mould in the processing of plastics.

Material Basis

• Modified Solvent-Based Polyurethane Matrix.

Color

• Clear to Yellow (Transparent when Dry).

PH-Values

• Neutral.

Package Sizes:

• 6-L-White Tin Can (5. 0 kg), 30-L-Hobbock (20. 00 kg)

Storage

Minimum of 12 months at a temperature between 5 degrees Celsius to 35 degrees Celsius when stored in tightly sealed original container. Protect against frost and higher temperatures. In the event of storage beyond expiration date, test the material prior to use. Tightly air seal opened containers to preserve product life. Ensure sufficient ventilation in product storage areas.

Preparation/Mixture

2-Part System: Mix 4. 5 part of Component A (basis) with 1 part Component B (hardening agent). Stir thoroughly. Drop-time 3-4 hours at room temperature.

Application

Apply with spray, dip coating, or brush until a thin coating becomes visible.

Application Temperatures

Apply product at air and object surface temperatures between 5 degrees Celsius and 35 degrees Celsius. Product is dust-dry within 2 hours and resilient after 2 days. Thermal hardening requires approximately 1 hour at 80 Degrees Celsius. Maximum thermal resistance is 150 Degrees Celsius. Variations from these external conditions could influence the hardening time.

Use and Application

By spray application apply approximately 50-70 ml/m2.

Safety and Protective Measures

During application and use, carefully follow the instructions and safety precautions on the package label as well as the pertinent safety and accident instructions of appropriate occupational and trade associations. For further detailed instructions, see safety data sheets.

Cleaning of Tools

Clean tools using alcohol/thinner.

Improvements and Second coatings

Coating improvements are not possible. New coatings: abrasive finishing of the Nano-E2C 106 coating after hardening. Prior to hardening, the lacquer can possibly be scraped or rubbed off using thinner. Cleaning of Coated Surfaces

Use customary household cleaners. Avoid: strong abrasive alkaline cleaners.

Disposal of Waste/Remains

Dispose of material residues according to local and/or state regulation for paints and lacquers.

Technical Data

Salt Spray (DINN EN ISO 9227 NSS): 1000h

CASS (DIN EN ISO 9227 CASS): 240h

Weathering (DIN EN ISO 4892-3: 4h UV-B 69°C: 50h 4h water condensation 50°C

Climate change DBL 7906: 15min 23°C, 4h-30°C: 10 cykles15 min 23°C; 4h 80°C: 30 min 40°C 98% rel humidity

Acid/Base Resistance: pH 1 to pH 12

Pencil Hardness: B

Temperature Resistance: Continuous up to 150 Degrees C.

Surface Energy: 17 MN/m